Recently,  180 tons a certain brand of 800 mpa grade DP steel, dual phase steel) in the three cold rolled back units offline smoothly, surface quality and stable performance values are within the scope of the internal control, so far, three cold rolling has formed 500 mpa and 600 mpa and 600 mpa (dual phase steel) a full range of DP steel mass stable supply ability.

DP steel, dual phase steel) for its low showed initial strain hardening rate, high, and the advantages of good strength and extensibility of the match, has developed into a kind of good formability new stamping with high strength steel, mainly used in car manufacturing.

In front of the unit independent integration, to stable 800 mpa grade of dual phase steel task is not an easy thing.Experienced a failure, after the factory for the whole process of this steel grade process screening and analysis, finally found the root cause and make the appropriate adjustments to part of the process.Will track at the same time, strictly implement the "two" standard, careful operation, the final 11 volume amounted to 180 tons of bulk rolled off the production line, surface and performance all comply with internal control standard.